Trimer catalyst additives for improving foam processability

ABSTRACT

The present invention provides trimerization catalyst compositions and methods to produce a polyisocyanurate/polyurethane foam using such trimerization catalyst compositions. The catalyst composition is the contact product of at least one α,β-unsaturated carboxylate salt and at least one second carboxylate salt.

BACKGROUND OF THE INVENTION

The present invention relates generally to catalyst systems, polyisocyanurate/polyurethane (PIR/PUR) foam formulations, and methods of making PIR/PUR foams.

Typically, polyisocyanurate/polyurethane (PIR/PUR) foams are made by reacting a polyol and a polyisocyanate in the presence of a catalyst. Additional additives can be present. PIR/PUR foam products have excellent thermal stability and flame resistance. Isocyanurates retain their strength to temperatures of about 160° C. and are resistant to most organic solvents, acids, alkali, ultraviolet light, and humidity.

Certain carboxylate salts, such as, for example, certain alkali metal carboxylate salts, have been used as catalysts in the production of PIR/PUR foams. The use of commercially available alkali metal carboxylate salt catalysts, however, often leads to undesirable foam processing problems which are particularly significant in continuous foam operations. A distinctive “step” is observed, which is normally associated with the onset of the trimerization process, when measuring the rise speed profile of the foam, or by plotting the foam height versus time. This trimerization “step” causes a significant change in the speed of the foam rise; in essence, the foam expands at two different rates during the foaming process. In a continuous polyisocyanurate/polyurethane foam lamination operation, it is difficult to adjust the speed of the production unit to match the change in the speed of the foam rise. The result can be foam overpacking or foam back flow. This undesirable rapid rise in foam height is particularly troublesome when processing polyisocyanurate/polyurethane formulations at a high Isocyanate Index. That is, the change in the rate of foam rise is much more dramatic at a higher Isocyanate Index. Consequently, it is a technical challenge to produce desirable low flammability foam products, with a high isocyanate index, when using conventional alkali metal carboxylate salt catalysts.

As compared to alkali metal carboxylate salt catalysts, commercially available polyisocyanurate trimerization catalysts based on hydroxyalkylammonium carboxylate salts show different processability in continuous operations. They provide a smoother rate of rise profile and have a less significant trimerization “step.” That is, the rate of foam rise is more consistent, even at a higher Isocyanate Index. However, hydroxyalkylammonium carboxylate salt catalysts often can be unstable at temperatures above about 100° C., decomposing into volatile amine by-products. This decomposition process causes the release of volatile amines and can impart an undesirable amine odor to finished foam products. The polymerization reactions that produce PIR/PUR foam are highly exothermic, often leading to foam processing temperatures in excess of 100° C. Hence, hydroxyalkylammonium carboxylate salt catalysts can provide more predictable foam processability, but sometimes at the expense of a foam product with an undesirable amine odor.

Thus, there exists a need for a catalyst composition that can offer a smooth rise profile—foam height versus time—for producing PIR/PUR foams in continuous operations. Further, the catalyst composition also should perform well in foam formulations with a high Isocyanate Index. At the same time, the catalyst composition should provide equivalent or faster surface cure when compared to commercially available catalyst systems, such that the foam products made with the catalyst composition can have reduced surface friability and enhanced surface adherence during the manufacture of finished products such as laminated foam panels. Optionally, depending upon the selection of the catalyst components, the catalyst composition can be thermally stable at the temperatures which PIR/PUR foams normally encounter during manufacturing, and produce foams that are substantially free of volatile amines and/or amine odors.

BRIEF SUMMARY OF THE INVENTION

The present invention provides a novel catalyst composition comprising the contact product of at least one a,β-unsaturated carboxylate salt and at least one second carboxylate salt. The at least one a,β-unsaturated carboxylate salt employed to form the catalyst composition of the present invention can be a compound of the formula

wherein:

X, Y, and Z are selected independently from a C₁-C₃₆ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; —CO₂H; —CO₂M¹; or a hydrogen atom; and

M¹ in each occurrence is selected independently from

-   -   (i) an alkali metal ion,     -   (ii) an alkaline earth metal ion, or     -   (iii) a quaternary ammonium ion.

In accordance with the present invention, the at least one second carboxylate salt includes, but is not limited to, an alkali metal carboxylate salt, an alkaline earth metal carboxylate salt, a quaternary ammonium carboxylate salt, or any combination thereof. Further, the at least one second carboxylate salt employed to form the catalyst composition of the present invention can be a compound of the formula A-CO₂M² wherein:

A is a hydrogen atom, or a C₁-C₁₇ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; and

M² is

-   -   (i) an alkali metal ion,     -   (ii) an alkaline earth metal ion, or     -   (iii) a quaternary ammonium ion.

In addition, the present invention provides a method for preparing a polyisocyanurate/polyurethane (PIR/PUR) foam which comprises contacting at least one polyisocyanate with at least one active hydrogen-containing compound, in the presence of at least one blowing agent and an effective amount of a catalyst composition comprising a contact product of at least one α,β-unsaturated carboxylate salt and at least one second carboxylate salt.

The catalyst composition of the present invention offers a substantially consistent foam height rise versus time—even at a high Isocyanate Index—and provides a faster surface cure during the preparation of PIR/PUR foams. In another aspect of the present invention, the catalyst composition can be thermally stable at standard foam processing temperatures, producing PIR/PUR foams which are substantially free of volatile amines and/or amine odors.

DEFINITIONS

The following definitions are provided in order to aid those skilled in the art in understanding the detailed description of the present invention.

-   -   PIR—Polyisocyanurate.     -   PUR—Polyurethane.     -   Isocyanate Index—The actual amount of polyisocyanate used         divided by the theoretically required stoichiometric amount of         polyisocyanate required to react with all the active hydrogen in         the reaction mixture, multiplied by 100. Also known as (Eq         NCO/Eq of active hydrogen)×100.     -   pphp—parts by weight per hundred weight parts polyol.     -   DABCO® K15 catalyst from Air Products and Chemicals, Inc. (APCI)         is a 70% solution of an alkali metal carboxylate salt, potassium         2-ethylhexanoate (also known potassium octoate), in diethylene         glycol.     -   DABCO TMR® catalyst from APCI is a 75% solution of         2-hydroxypropyltrimethylammonium octoate in ethylene glycol     -   DABCO® K2097 catalyst from APCI is a 30% solution of an alkali         metal carboxlate salt, potassium acetate, in diethylene glycol.     -   Polycat® 5 catalyst from APCI is a urethane catalyst, known         chemically as pentamethyldiethylenetriamine.

BRIEF DESCRIPTION OF SEVERAL VIEWS OF THE DRAWINGS

FIG. 1 presents a plot of the normalized foam height versus time for carboxylate salt catalyst 1, DABCO® K15 catalyst, and DABCO TMR® catalyst, at an Isocyanate Index of about 500.

FIG. 2 presents a plot of the rate of foam rise speed versus time for carboxylate salt catalyst 1, DABCO® K15 catalyst, and DABCO TMR® catalyst, at an Isocyanate Index of about 500.

FIG. 3 presents a plot of the normalized foam height versus time for α,β-unsaturated carboxylate salt catalyst 2, DABCO® K15 catalyst, and DABCO TMR® catalyst, at an Isocyanate Index of about 500.

FIG. 4 presents a plot of the normalized foam height versus time for inventive catalyst 3—comprising one α,β-unsaturated carboxylate salt and one second carboxylate salt, DABCO® K15 catalyst, and DABCO TMR® catalyst, at an Isocyanate Index of about 500.

FIG. 5 presents a plot of the rate of foam rise speed versus time for inventive catalyst 3—comprising one α,β-unsaturated carboxylate salt and one second carboxylate salt, DABCO® K15 catalyst, and DABCO TMR® catalyst, at an Isocyanate Index of about 500.

FIG. 6 presents a plot of the foam height versus time for inventive catalyst combinations of the DABCO® K15 catalyst (a second carboxylate salt) and catalyst 2 (an α,β-unsaturated carboxylate salt), at an Isocyanate Index of about 270.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is directed to a novel catalyst composition comprising at least one α,β-unsaturated carboxylate salt and at least one second carboxylate salt. This novel catalyst system can be used as a polyisocyanate trimerization catalyst system for producing polyisocyanurate/polyurethane (PIR/PUR) foams. Also, the present invention provides a method for preparing a PIR/PUR foam which comprises contacting at least one polyisocyanate with at least one active hydrogen-containing compound, in the presence of at least one blowing agent and an effective amount of a catalyst composition comprising a contact product of at least one α,β-unsaturated carboxylate salt and at least one second carboxylate salt. Additionally, rigid PIR/PUR foams can be produced with the novel catalyst system of the present invention by several methods known within the art.

The catalyst composition of the present invention can be used to trimerize isocyanates to produce isocyanurates. Generally, any amount of the at least one α,β-unsaturated carboxylate salt can be used in the catalyst composition of this invention. As used in practice, catalyst systems for PIR/PUR foams are typically solutions of carboxylate salts in, for example, a diluent such as ethylene glycol. When weight ratios or molar ratios of the catalyst component are discussed, these ratios exclude the effect of the diluent, unless specified otherwise. For example, if 10 grams of a 50% solution of potassium acetate catalyst in ethylene glycol were used in a given application, the amount of the potassium acetate salt catalyst would equal 5 grams. Hence, 5 grams of that catalyst component would be used in determining any weight ratios.

Applicants disclose several types of ranges in the present invention. These include, but are not limited to, a range of temperatures; a range of catalyst component weight ratios; a range of number of atoms; a range of foam density; a range of Isocyanate Index; and a range of pphp for the blowing agent, water, surfactant, flame retardant, urethane catalyst, and catalyst composition of the present invention. When Applicants disclose or claim a range of any type, Applicants' intent is to disclose or claim individually each possible number that such a range could reasonably encompass, as well as any sub-ranges and combinations of sub-ranges encompassed therein. For example, when the Applicants disclose or claim a chemical moiety having a certain number of carbon atoms, Applicants' intent is to disclose or claim individually every possible number that such a range could encompass, consistent with the disclosure herein. For example, the disclosure that “A” can be an alkyl group having up to 17 carbon atoms, or in alternative language a C₁ to C₁₇ alkyl group, as used herein, refers to an “A” group that can be selected independently from a alkyl group having 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, or 17 carbon atoms, as well as any range between these two numbers (for example, a C₃ to C₈ alkyl group), and also including any combination of ranges between these two numbers (for example, a C₃ to C₅ and C₇ to C₁₀ alkyl group). Likewise, this applies to all other carbon ranges disclosed herein, for example, C₁ to C₃₆ ranges for X, Y, and Z; alkoxy groups having up to 10 carbon atoms; etc.

Similarly, by the disclosure that a weight ratio typically spans a range from about 0.1:1 to about 10:1, for example, Applicants intend to recite that the weight ratio can be selected from about 0.1:1, about 0.2:1, about 0.3:1, about 0.4:1, about 0.5:1, about 0.6:1, about 0.7:1, about 0.8:1, about 0.9:1, about 1:1, about 2:1, about 3:1, about 4:1, about 5:1, about 6:1, about 7:1, about 8:1, about 9:1, or about 10:1. Likewise, this applies to other weight ratio ranges disclosed herein, such as a catalyst component weight ratio from about 0.02:1 to about 50:1, for example.

Applicants intent with regard to the pphp of a specific component in a foam formulation would be construed similarly. As an example, for a range of 0 to about 5 pphp, the pphp can be selected from 0, about 0.1, about 0.2, about 0.3, about 0.4, about 0.5, about 0.6, about 0.7, about 0.8, about 0.9, about 1, about 2, about 3, about 4, or about 5. All other ranges disclosed herein should be interpreted in manner similar to these three examples.

Applicants reserve the right to proviso out or exclude any individual members of any such group, including any sub-ranges or combinations of sub-ranges within the group, that may be claimed according to a range or in any similar manner, if for any reason Applicants choose to claim less than the full measure of the disclosure, for example, to account for a reference that Applicants may be unaware of at the time of the filing of the application. Further, Applicants reserve the right to proviso out or exclude any individual substituents, analogs, compounds, ligands, structures, or groups thereof, or any members of a claimed group, if for any reason Applicants choose to claim less than the full measure of the disclosure, for example, to account for a reference that Applicants may be unaware of at the time of the filing of the application.

In one aspect of the present invention, the weight ratio of the at least one α,β-unsaturated carboxylate salt to the at least one second carboxylate salt can vary based on the desired properties of the PIR/PUR foam formulation or the Isocyanate Index. For example, the weight ratio of the at least one α,β-unsaturated carboxylate salt to the at least one second carboxylate salt is from about 0.02:1 to about 50:1. In another aspect, the weight ratio of the at least one α,β-unsaturated carboxylate salt to the at least one second carboxylate salt is from about 0.03:1 to about 30:1. In a further aspect, the weight ratio of the at least one α,β-unsaturated carboxylate salt to the at least one second carboxylate salt is from about 0.04:1 to about 25:1, about 0.05:1 to about 20:1, about 0.1:1 to about 10:1, about 0.2:1 to about 5:1, about 0.25:1 to about 4:1, about 0.5:1 to about 2:1, or about 0.75:1 to about 1.5:1.

Another aspect of the present invention provides a thermally stable catalyst system. When used to describe this feature, a compound is defined as thermally stable at a given temperature when it does not decompose or release volatile amines and/or related amine odors at the given temperature. A hydroxyalkylammonium salt catalyst, such as the DABCO TMR® catalyst, can become unstable when the PIR/PUR foam temperature reaches above about 100° C. during foam processing. At these elevated temperatures, due to the nature of the quaternary amine salt, the DABCO TMR® catalyst can release volatile amine components. Catalyst compositions of the present invention which are based on quaternary ammonium salts are thermally stable if they do not have either functional groups (e.g., hydroxyl) or hydrogen on the carbon atom at the β-position relative to the quaternary nitrogen.

Thus, thermally stable catalyst compositions of the present invention include, but are not limited to, alkali metal α,β-unsaturated carboxylate salts, alkali metal carboxylate salts, alkaline earth metal α,β-unsaturated carboxylate salts, alkaline earth metal carboxylate salts, or any combination thereof. Quaternary ammonium salts with thermal stability include, but are not limited to, tetramethylammonium pivalate, tetramethylammonium acrylate, tetraethylammonium acrylate, tetrapropylammonium acrylate, tetrabutylammonium acrylate, tetramethylammonium methacrylate, tetraethylammonium methacrylate, tetrapropylammonium methacrylate, tetrabutylammonium methacrylate, mono-tetramethylammonium fumarate, bis-tetramethylammonium fumarate, potassium tetramethylammonium fumarate, mono-tetraethylammonium fumarate, bis-tetraethylammonium fumarate, potassium tetraethylammonium fumarate, mono-tetrapropylammonium fumarate, bis-tetrapropylammonium fumarate, potassium tetrapropylammonium fumarate, mono-tetrabutylammonium fumarate, bis-tetrabutylammonium fumarate, potassium tetrabutylammonium fumarate, mono-potassium maleate, bis-potassium maleate, mono-tetramethylammonium maleate, bis-tetramethylammonium maleate, potassium tetramethylammonium maleate, mono-tetraethylammonium maleate, bis-tetraethylammonium maleate, potassium tetraethylammonium maleate, mono-tetrapropylammonium maleate, bis-tetrapropylammonium maleate, potassium tetrapropylammonium maleate, mono-tetrabutylammonium maleate, bis-tetrabutylammonium maleate, potassium tetrabutylammonium maleate, tetramethylammonium formate, tetramethylammonium acetate, tetramethylammonium propionate, tetramethylammonium butanoate, tetramethylammonium pentanoate, tetramethylammonium hexanoate, tetramethylammonium heptanoate, tetramethylammonium octoate, tetramethylammonium 2-ethylhexanoate, tetramethylammonium decanoate, tetramethylammonium butyrate, tetramethylammonium isobutyrate, tetramethylammonium nonante, tetramethylammonium stearate, tetramethylammonium neodecanoate, tetramethylammonium neoheptanoate, and the like.

In one aspect of the present invention, the catalyst composition comprising at least one α,β-unsaturated carboxylate salt and at least one second carboxylate salt, has thermal stability up to about 150° C., wherein no or substantially no volatile amine compounds are emitted. Typical foam temperatures resulting from the exothermic reactions during the processing of PIR/PUR foam can be in the range of about 80° C. to about 150° C. In a further aspect, the catalyst system of the present invention has thermal stability up to about 175° C., about 200° C., about 220° C., about 240° C., or about 250° C.

The carboxylate salts of the catalyst composition of the present invention can be produced, for example, by the reaction of an organic acid with an alkali hydroxide. In another aspect of the present invention, the carboxylate salt can be produced by the reaction of an organic acid with a tetraalkylammonium hydroxide, or a reaction of an organic acid with a tertiary amine followed by a reaction with an epoxy compound. The latter reaction with an epoxy can lead to a hydroxyalkyl quaternary compound which is unstable at elevated temperatures.

The term “contact product” is used herein to describe compositions wherein the catalyst components are contacted together in any order, in any manner, and for any length of time. For example, the components can be contacted by blending or mixing. Further, contacting of any catalyst component can occur in the presence or absence of any other component of the foam formulations described herein. In one aspect of the present invention, the catalyst composition can be prepared by combining or contacting the at least one α,β-unsaturated carboxylate salt and at least one second carboxylate salt. This typically occurs in solution form. In another aspect, the catalyst composition can be prepared by first mixing the respective carboxylic acids, followed by neutralization to form the corresponding salts.

While compositions and methods are described in terms of “comprising” various components or steps, the compositions and methods can also “consist essentially of” or “consist of” the various components or steps.

α,β-Unsaturated Carboxylate Salts

Catalyst compositions of the present invention can be formed by employing at least one a,β-unsaturated carboxylate salt having the formula

wherein:

X, Y, and Z are selected independently from a C₁-C₃₆ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; —CO₂H; —CO₂M¹; or a hydrogen atom; and

M¹ in each occurrence is selected independently from

-   -   (i) an alkali metal ion,     -   (ii) an alkaline earth metal ion, or     -   (iii) a quaternary ammonium ion.

Unless otherwise specified, alkyl and alkenyl groups described herein are intended to include all structural isomers, linear or branched, of a given structure; for example, all enantiomers and all diasteriomers are included within this definition. As an example, unless otherwise specified, the term propyl is meant to include n-propyl and iso-propyl, while the term butyl is meant to include n-butyl, iso-butyl, t-butyl, sec-butyl, and so forth. Similarly, substituted alkyl, alkenyl, aryl, and aralkyl groups described herein are intended to include substituted analogs of a given structure. For example, the substituents on alkyl, alkenyl, aryl, and aralkyl groups can include, but are not limited to, halides; hydroxyl groups; amino groups; alkoxy, alkylamino, or dialkylamino groups having up to 10 carbon atoms; or combinations thereof.

Non-limiting examples of alkyl groups which can be present in the at least one α,β-unsaturated carboxylate salt include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, or decyl, and the like. Examples of alkenyl groups within the scope of the present invention include, but are not limited to, ethenyl, propenyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, and the like. Aryl and aralkyl (aralkyl is defined as an aryl-substituted alkyl or arylalkyl) groups include phenyl, alkyl-substituted phenyl, naphthyl, alkyl-substituted naphthyl, and the like. For example, non-limiting examples of aryl and aralkyl groups useful in the present invention include, but are not limited to, phenyl, tolyl, benzyl, dimethylphenyl, trimethylphenyl, phenylethyl, phenylpropyl, phenylbutyl, propyl-2-phenylethyl, and the like.

In one aspect of the present invention, X, Y, and Z are selected independently from a hydrogen atom, methyl, ethyl, propyl, butyl, pentyl, hexyl, phenyl, tolyl, benzyl, —CO₂H, or —CO₂M¹. In another aspect, M¹ in each occurrence is an ion of lithium, potassium, sodium, rubidium, magnesium, or calcium, or a quaternary ammonium ion. Quaternary ammonium ions useful in the present invention include, but are not limited to, tetramethylammonium, tetraethylammonium, tetrapropylammonium, tetrabutylammonium, trimethyl(2-hydroxypropyl)ammonium, triethyl(2-hydroxypropyl)ammonium, tripropyl(2-hydroxypropyl)ammonium, tributyl(2-hydroxypropyl)ammonium, trimethyl(2-hydroxyethyl)ammonium, triethyl(2-hydroxyethyl)ammonium, tripropyl(2-hydroxyethyl)ammonium, tributyl(2-hydroxyethyl)ammonium, dimethylbenzyl(2-hydroxypropyl)ammonium, dimethylbenzyl(2-hydroxyethyl)ammonium, and the like, or any combination thereof. In a further aspect of the present invention, M¹ is a potassium ion.

Salts and mixtures of salts of acrylic acid, methacrylic acid, fumaric acid, maleic acid, and the like, are within the scope of the present invention. Suitable α,β-unsaturated carboxylate salts useful in the present invention include, but are not limited to, potassium acrylate, tetramethylammonium acrylate, tetraethylammonium acrylate, tetrapropylammonium acrylate, tetrabutylammonium acrylate, potassium methacrylate, tetramethylammonium methacrylate, tetraethylammonium methacrylate, tetrapropylammonium methacrylate, tetrabutylammonium methacrylate, mono-potassium fumarate, bis-potassium fumarate, mono-tetramethylammonium fumarate, bis-tetramethylammonium fumarate, potassium tetramethylammonium fumarate, mono-tetraethylammonium fumarate, bis-tetraethylammonium fumarate, potassium tetraethylammonium fumarate, mono-tetrapropylammonium fumarate, bis-tetrapropylammonium fumarate, potassium tetrapropylammonium fumarate, mono-tetrabutylammonium fumarate, bis-tetrabutylammonium fumarate, potassium tetrabutylammonium fumarate, mono-potassium maleate, bis-potassium maleate, mono-tetramethylammonium maleate, bis-tetramethylammonium maleate, potassium tetramethylammonium maleate, mono-tetraethylammonium maleate, bis-tetraethylammonium maleate, potassium tetraethylammonium maleate, mono-tetrapropylammonium maleate, bis-tetrapropylammonium maleate, potassium tetrapropylammonium maleate, mono-tetrabutylammonium maleate, bis-tetrabutylammonium maleate, potassium tetrabutylammonium maleate, trimethyl(2-hydroxyethyl)ammonium acrylate, triethyl(2-hydroxyethyl)ammonium acrylate, tripropyl(2-hydroxyethyl)ammonium acrylate, tributyl(2-hydroxyethyl)ammonium acrylate, dimethylbenzyl(2-hydroxypropyl)ammonium acrylate, dimethylbenzyl(2-hydroxyethyl)ammonium acrylate, trimethyl(2-hydroxyethyl)ammonium methacrylate, triethyl(2-hydroxyethyl)ammonium methacrylate, tripropyl(2-hydroxyethyl)ammonium methacrylate, tributyl(2-hydroxyethyl)ammonium methacrylate, dimethylbenzyl(2-hydroxypropyl)ammonium methacrylate, dimethylbenzyl(2-hydroxyethyl)ammonium methacrylate, bis-(trimethyl(2-hydroxyethyl)ammonium) maleate, bis-(triethyl(2-hydroxyethyl)ammonium)maleate, bis-(tripropyl(2-hydroxyethyl)ammonium) maleate, bis-(tributyl(2-hydroxyethyl)ammonium) maleate, bis-(dimethylbenzyl(2-hydroxypropyl)ammonium)maleate, bis-(dimethylbenzyl(2-hydroxyethyl)ammonium)maleate, bis-(trimethyl(2-hydroxyethyl)ammonium)fumarate, bis-(triethyl(2-hydroxyethyl)ammonium)fumarate, bis-(tripropyl(2-hydroxyethyl)ammonium)fumarate, bis-(tributyl(2-hydroxyethyl)ammonium)fumarate, bis-(dimethylbenzyl(2-hydroxypropyl)ammonium)fumarate, bis-(dimethylbenzyl(2-hydroxyethyl)ammonium)fumarate, and the like, or any combination thereof. In another aspect of the present invention, the α,β-unsaturated carboxylate salt is potassium acrylate.

Second Carboxylate Salts

Catalyst compositions of the present invention can be formed by employing at least one second carboxylate salt. Such carboxylate salt includes, but is not limited to, an alkali metal carboxylate salt, an alkaline earth metal carboxylate salt, a quaternary ammonium carboxylate salt, or any combination thereof. Further, as discussed above, catalyst compositions of the present invention can comprise at least one second carboxylate salt having the formula, A-CO₂M² wherein:

A is a hydrogen atom, or a C₁-C₁₇ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; and

M² is

-   -   (i) an alkali metal ion,     -   (ii) an alkaline earth metal ion, or     -   (iii) a quaternary ammonium ion.

Unless otherwise specified, alkyl and alkenyl groups described herein are intended to include all structural isomers, linear or branched, of a given structure; for example, all enantiomers and all diasteriomers are included within this definition. As an example, unless otherwise specified, the term propyl is meant to include n-propyl and iso-propyl, while the term butyl is meant to include n-butyl, iso-butyl, t-butyl, sec-butyl, and so forth. Similarly, substituted alkyl, alkenyl, aryl, and aralkyl groups described herein are intended to include substituted analogs of a given structure. For example, the substituents on alkyl, alkenyl, aryl, and aralkyl groups can include, but are not limited to, halides; hydroxyl groups; amino groups; alkoxy, alkylamino, or dialkylamino groups having up to 10 carbon atoms; or combinations thereof.

Non-limiting examples of alkyl groups which can be present in the at least one second carboxylate salt include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, or decyl, and the like. Examples of alkenyl groups within the scope of the present invention include, but are not limited to, ethenyl, propenyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, and the like. Aryl and aralkyl (aralkyl is defined as an aryl-substituted alkyl or arylalkyl) groups include phenyl, alkyl-substituted phenyl, naphthyl, alkyl-substituted naphthyl, and the like. For example, non-limiting examples of aryl and aralkyl groups useful in the present invention include, but are not limited to, phenyl, tolyl, benzyl, dimethylphenyl, trimethylphenyl, phenylethyl, phenylpropyl, phenylbutyl, propyl-2-phenylethyl, and the like.

In one aspect of the present invention, A is a hydrogen atom, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, or octyl. In another aspect, M² is an ion of lithium, potassium, sodium, rubidium, magnesium, or calcium, or a quaternary ammonium ion. Quaternary ammonium ions useful in the present invention include, but are not limited to, tetramethylammonium, tetraethylammonium, tetrapropylammonium, tetrabutylammonium, trimethyl(2-hydroxypropyl)ammonium, triethyl(2-hydroxypropyl)ammonium, tripropyl(2-hydroxypropyl)ammonium, tributyl(2-hydroxypropyl)ammonium, trimethyl(2-hydroxyethyl)ammonium, triethyl(2-hydroxyethyl)ammonium, tripropyl(2-hydroxyethyl)ammonium, tributyl(2-hydroxyethyl)ammonium, dimethylbenzyl(2-hydroxypropyl)ammonium, dimethylbenzyl(2-hydroxyethyl)ammonium, and the like, or any combination thereof. In a further aspect of the present invention, M² is a potassium ion.

In one aspect of the present invention, the at least one second carboxylate salt includes, but is not limited to, alkali metal carboxylate salts, alkaline earth metal carboxylate salts, quaternary ammonium carboxylate salts, or combinations thereof. Suitable alkali metal carboxylate salts of the present invention include, but are not limited to, potassium pivalate, potassium formate, potassium acetate, potassium propionate, potassium butanoate, potassium pentanoate, potassium hexanoate, potassium neohexanoate, potassium heptanoate, potassium octoate, potassium neooctoate, potassium 2-ethylhexanoate, potassium decanoate, potassium butyrate, potassium isobutyrate, potassium nonante, potassium stearate, potassium neodecanoate, potassium neoheptanoate, sodium octoate, lithium stearate, sodium caprioate, lithium octoate, and the like, or any combination thereof. In another aspect, the at least one second carboxylate salt is potassium pivalate, potassium acetate, potassium octoate, potassium 2-ethylhexanoate, or any combination thereof.

In yet another aspect, the at least one second carboxylate salt is a salt of a carboxylic acid. Suitable carboxylic acids include, but are not limited to, formic, acetic, propionic, butanoic, butyric, isobutyric, pivalic, pentanoic, hexanoic, neohexanoic, heptanoic, neoheptanoic, octanoic, neooctanoic, 2-ethyl-hexanoic, nonanoic, neononanoic, decanoic, neodecanoic, undecanoic, neoundecanoic, dodecanoic, neododecanoic, myristic, palmitic, stearic, oleic, linoleic, linolenic, ricinoleic, and the like, mixtures thereof, or any combination thereof.

Polyisocyanates

Polyisocyanates that are useful in the PIR/PUR foam formation process include, but are not limited to, hexamethylene diisocyanate, isophorone diisocyanate, phenylene diisocyante, toluene diisocyanate (TDI), diphenyl methane diisocyanate isomers (MDI), hydrated MDI and 1,5-naphthalene diisocyanate. For example, 2,4-TDI, 2,6-TDI, and mixtures thereof, can be readily employed in the present invention. Other suitable mixtures of diisocyanates include, but are not limited to, those known in the art as crude MDI, or PAPI, which contain 4,4′-diphenylmethane diisocyanate along with other isomeric and analogous higher polyisocyanates. In another aspect of this invention, prepolymers of polyisocyanates comprising a partially pre-reacted mixture of polyisocyanates and polyether or polyester polyol are suitable. In still another aspect, the polyisocyanate comprises MDI, or consists essentially of MDI or mixtures of MDI's.

The catalyst system and the method of producing PIR/PUR foam of the present invention can be used to produce many types of foam. This catalyst system is also useful in the formation of foam products for rigid and flame retardant applications, which usually require a high Isocyanate Index. As defined previously, Isocyanate Index is the actual amount of polyisocyanate used divided by the theoretically required stoichiometric amount of polyisocyanate required to react with all the active hydrogen in the reaction mixture, multiplied by 100. For purposes of the present invention, Isocyanate Index is represented by the equation: Isocyanate Index=(Eq NCO/Eq of active hydrogen)×100, wherein Eq NCO is the number of NCO functional groups in the polyisocyanate, and Eq of active hydrogen is the number of equivalent active hydrogen atoms.

Foam products which are produced with an Isocyanate Index from about 80 to about 800 are within the scope of this invention. In accordance with other aspects of the present invention, the Isocyanate Index is from about 100 to about 700, from about 150 to about 650, from about 200 to about 600, or from about 250 to about 500.

Polyols

Active hydrogen-containing compounds for use with the foregoing polyisocyanates in forming the polyisocyanurate/polyurethane foams of this invention can be any of those organic compounds having at least two hydroxyl groups such as, for example, polyols. Polyols that are typically used in PIR/PUR foam formation processes include polyalkylene ether and polyester polyols. The polyalkylene ether polyol includes the poly(alkyleneoxide) polymers such as poly(ethyleneoxide) and poly(propyleneoxide) polymers and copolymers with terminal hydroxyl groups derived from polyhydric compounds, including diols and triols, These include, but are not limited to, ethylene glycol, propylene glycol, 1,3-butane diol, 1,4-butane diol, 1,6-hexane diol, neopentyl glycol, diethylene glycol, dipropylene glycol, pentaerythritol, glycerol, diglycerol, trimethylol propane, cyclohexane diol, and sugars such as sucrose and like low molecular weight polyols.

Amine polyether polyols can be used in the present invention. These can be prepared when an amine such as, for example, ethylenediamine, diethylenetriamine, tolylenediamine, diphenylmethanediamine, or triethanolamine is reacted with ethylene oxide or propylene oxide.

In another aspect of the present invention, a single high molecular weight polyether polyol, or a mixture of high molecular weight polyether polyols, such as mixtures of different multifunctional materials and/or different molecular weight or different chemical composition materials can be used.

In yet another aspect of the present invention, polyester polyols can be used, including those produced when a dicarboxylic acid is reacted with an excess of a diol. Non-limiting examples include adipic acid or phathalic acid or phthalic anhydride reacting with ethylene glycol or butanediol. Polyols useful in the present invention can be produced by reacting a lactone with an excess of a diol, for example, caprolactone reacted with propylene glycol. In a further aspect, active hydrogen-containing compounds such as polyester polyols and polyether polyols, and mixtures thereof, are useful in the present invention.

Blowing Agents

Blowing agents that can be used alone or in combination in the PIR/PUR foam formation process include, but are not limited to, water, methylene chloride, acetone, chlorofluorocarbons (CFCs), hydrofluorocarbons (HFCs), hydrochlorofluorocarbons (HCFCs), and hydrocarbons. Non-limiting examples of HFCs include HFC-245fa, HFC-134a, and HFC-365. Illustrative examples of HCFCs include HCFC-141b, HCFC-22, and HCFC-123. Exemplary hydrocarbons include n-pentane, isopentane, cyclopentane, and the like, or any combination thereof.

The amount of blowing agent used can vary based on, for example, the intended use and application of the foam product and the desired foam stiffness and density. In the foam formulation and method for preparing a polyisocyanurate/polyurethane foam of the present invention, the blowing agent is present in amounts from about 10 to about 80 parts by weight per hundred weight parts polyol (pphp), from about 12 to about 60 pphp, from about 14 to about 40 pphp, or from about 16 to about 25 pphp. If water is present in the formulation, for use as a blowing agent or otherwise, water is present in amounts up to about 15 pphp. In other words, water can range from 0 to about 15 pphp. In another aspect, water can range from 0 to about 10 pphp, from 0 to about 8 pphp, from 0 to about 6 pphp, or from 0 to about 4 pphp.

Urethane Catalyst

Urethane catalysts accelerate the reaction to form polyurethanes, and can be used as a further component of the catalyst system of the present invention to produce polyisocyanurate/polyurethane foam. Urethane catalysts suitable for use herein include, but are not limited to, metal salt catalysts, such as organotins, and amine compounds, such as triethylenediamine (TEDA), N-methylimidazole, 1,2-dimethylimidazole, N-methylmorpholine (commercially available as the DABCO® NMM catalyst), N-ethylmorpholine (commercially available as the DABCO® NEM catalyst), triethylamine (commercially available as the DABCO® TETN catalyst), N,N′-dimethylpiperazine, 1,3,5-tris(dimethylaminopropyl)hexahydrotriazine (commercially available as the Polycat® 41 catalyst), 2,4,6-tris(dimethylaminomethyl)phenol (commercially available as the DABCO TMR® 30 catalyst), N-methyldicyclohexylamine (commercially available as the Polycat® 12 catalyst), pentamethyldipropylene triamine (commercially available as the Polycat® 77 catalyst), N-methyl-N′-(2-dimethylamino)-ethyl-piperazine, tributylamine, pentamethyldiethylenetriamine (commercially available as the Polycat® 5 catalyst), hexamethyltriethylenetetramine, heptamethyltetraethylenepentamine, dimethylaminocyclohexylamine (commercially available as the Polycat® 8 catalyst), pentamethyldipropylene-triamine, triethanolamine, dimethylethanolamine, bis(dimethylaminoethyl)ether (commercially available as the DABCO® BL19 catalyst), tris(3-dimethylamino)propylamine (commercially available as the Polycat® 9 catalyst), 1,8-diazabicyclo[5.4.0] undecene (commercially available as the DABCO® DBU catalyst) or its acid blocked derivatives, and the like, as well as any mixture thereof. Particularly useful as a urethane catalyst for foam applications related to the present invention is the Polycat® 5 catalyst, which is known chemically as pentamethyldiethylenetriamine.

For preparing a polyisocyanurate/polyurethane foam of the present invention, the urethane catalyst can be present in the formulation from 0 to about 10 pphp, from 0 to about 8 pphp, from 0 to about 6 pphp, from 0 to about 4 pphp, from 0 to about 2 pphp, or from 0 to about 1 pphp. In another aspect, the urethane catalyst is present from 0 to about 0.8 pphp, from 0 to about 0.6 pphp, from 0 to about 0.4 pphp, or from 0 to about 0.2 pphp.

Miscellaneous Additives

Depending upon on the requirements during foam manufacturing or for the end-use application of the foam product, various additives can be employed in the PIR/PUR foam formulation to tailor specific properties. These include, but are not limited to, cell stabilizers, flame retardants, chain extenders, epoxy resins, acrylic resins, fillers, pigments, or any combination thereof. It is understood that other mixtures or materials that are known in the art can be included in the foam formulations and are within the scope of the present invention.

Cell stabilizers include surfactants such as organopolysiloxanes. Silicon surfactants can be present in the foam formulation in amounts from about 0.5 to about 10 pphp, about 0.6 to about 9 pphp, about 0.7 to about 8 pphp, about 0.8 to about 7 pphp, about 0.9 to about 6 pphp, about 1 to about 5 pphp, or about 1.1 to about 4 pphp. Useful flame retardants include halogenated organophosphorous compounds and non-halogenated compounds. A non-limiting example of a halogenated flame retardant is trichloropropylphosphate (TCPP). For example, triethylphosphate ester (TEP) and DMMP are non-halogenated flame retardants. Depending on the end-use foam application, flame retardants can be present in the foam formulation in amounts from 0 to about 50 pphp, from 0 to about 40 pphp, from 0 to about 30 pphp, or from 0 to about 20 pphp. In another aspect, the flame retardant is present from 0 to about 15 pphp, 0 to about 10 pphp, 0 to about 7 pphp, or 0 to about 5 pphp. Chain extenders such as ethylene glycol and butane diol can also be employed in the present invention. Ethylene glycol, for instance, can also be present in the formulation as a diluent or solvent for the carboxylate salt catalysts of the present invention.

Polyisocyanurate/Polyurethane Foam

Formulation and Process

The present invention provides a method for preparing a polyisocyanurate/polyurethane (PIR/PUR) foam which comprises contacting at least one polyisocyanate with at least one active hydrogen-containing compound, in the presence of at least one blowing agent and an effective amount of a catalyst composition comprising a contact product of at least one α,β-unsaturated carboxylate salt and at least one second carboxylate salt. In accordance with the method of the present invention, PIR/PUR foams can be produced having a density from about 20 Kg/m³ to about 250 Kg/m³ (about 1.25 lb/ft³ to about 15.5 lb/ft³), or from about 24 Kg/m³ to about 60 Kg/m³ (about 1.5 lb/ft³ to about 3.75 lb/ft³).

In another aspect, the method of the present invention offers a substantially consistent foam height rise versus time—even at a high Isocyanate Index—that is highly desired for continuous foam manufacturing operations. The method for preparing PIR/PUR foams also provides equivalent or faster surface cure when compared to other commercially available catalyst systems, such that the PIR/PUR foam has enhanced surface adherence, useful for the production are articles such as laminated foam panels.

Optionally, in yet another aspect, the method of the present invention can produce PIR/PUR foams with no or substantially no undesirable amine odor. Dependent upon the selection of the specific at least one α,β-unsaturated carboxylate salt and the at least one second carboxylate salt, this method can provide thermal stability at the temperatures which PIR/PUR foams normally encounter during manufacturing, even those foams formulated with a high Isocyanate Index. In a further aspect, the method for preparing PIR/PUR foam has thermally stability up to about 150° C., or about 175° C., or about 200° C., or about 220° C., or about 240° C., or about 250° C. In a still further aspect, the method of the present invention produces PIR/PUR foam that is substantially free of volatile amines and/or amine odors.

The catalyst composition comprising at least one α,β-unsaturated carboxylate salt and at least one second carboxylate salt should be present in the foam formulation in a catalytically effective amount. In PIR/PUR foam formulations of the present invention, the catalyst composition is present in amounts from about 0.05 to about 10 parts by weight per hundred weight parts of the at least one active hydrogen-containing compound, excluding the weight contribution of the catalyst system diluent. In another aspect, the catalyst composition is present in amounts from about 0.4 to about 9 parts, or from about 0.8 to about 8 parts, by weight per hundred weight parts of the at least one active hydrogen-containing compound. If the at least one active hydrogen-containing compound is an at least one polyol, the catalyst composition is present in amounts from about 0.05 to about 10 parts by weight per hundred weight parts polyol (pphp). In another aspect, the catalyst composition is present in amounts from about 0.2 to about 9.5 pphp, about 0.4 to about 9 pphp, about 0.6 to about 8.5 pphp, or about 0.8 to about 8 pphp.

In the method of the present invention, the components of the foam formulation can be contacted or combined in any order. In one aspect, the at least one α,β-unsaturated carboxylate salt and the at least one second carboxylate salt are contacted with each other prior to being contacted with any of the at least one active hydrogen-containing compound, the at least one blowing agent, the at least one polyisocyanate, or any combination thereof. In another aspect, the at least one α,β-unsaturated carboxylate salt and the at least one second carboxylate salt are contacted with each other while being contacted with any of the at least one active hydrogen-containing compound, the at least one blowing agent, the at least one polyisocyanate, or any combination thereof. In yet another aspect, either the at least one α,β-unsaturated carboxylate salt or the at least one second carboxylate salt independently is contacted with any of the at least one active hydrogen-containing compound, the at least one blowing agent, the at least one polyisocyanate, or any combination thereof, prior to both salt types being contacted with each other. Given the number of components involved in PIR/PUR formulations, there are many different orders of contacting or combining the components, and one of skill in the art would realize that varying the order of addition of the components falls within the scope of the present invention. As well, for each of the different orders of combining the components of the foam formulation, the foam formulation of the present invention can further comprise at least one urethane catalyst. In addition, the method of producing PIR/PUR foams can further comprise the presence of at least one additive selected from at least one cell stabilizer, at least one flame retardant, at least one chain extender, at least one epoxy resin, at least one acrylic resin, at least one filler, at least one pigment, or any combination thereof.

In a further aspect of the present invention, a premix of ingredients other than the at least one polyisocyanate can be contacted first, followed by the addition of the at least one polyisocyanate. For example, the at least one active hydrogen-containing compound, the at least one blowing agent, and the catalyst composition of the present invention are contacted initially to form a premix. The premix is then contacted with the at least one polyisocyanate to produce PIR/PUR foams in accordance with the method of the present invention. In a still further aspect of the present invention, the same method can be employed, wherein the premix further comprises at least one urethane catalyst. Likewise, the premix can further comprise at least one additive selected from at least one cell stabilizer, at least one flame retardant, at least one chain extender, at least one epoxy resin, at least one acrylic resin, at least one filler, at least one pigment, or any combination thereof.

One aspect of the present invention provides a method for preparing a polyisocyanurate/polyurethane foam comprising (a) forming a premix comprising:

-   -   i) at least one active hydrogen-containing polyol;     -   ii) about 10 to about 80 parts by weight per hundred weight         parts of the polyol (pphp) blowing agent;     -   iii) about 0.5 to about 10 pphp silicon surfactant;     -   iv) zero to about 10 pphp water;     -   v) zero to about 50 pphp flame retardant;     -   vi) zero to about 10 pphp urethane catalyst; and     -   vii) about 0.05 to about 10 pphp of a catalyst composition         comprising at least one α,β-unsaturated carboxylate salt and at         least one second carboxylate salt; and         (b) contacting the premix with at least one polyisocyanate at an         Isocyanate Index from about 80 to about 800.

EXAMPLES

The foams of the following examples were produced by adding the catalyst of the present invention into a premix of the polyol, flame retardant (TCPP), surfactant, urethane catalyst (Polycat® 5 catalyst), and blowing agent (n-pentane), in a 32-oz (951 ml) metal cup. This composition was mixed for about 10 seconds (s) at about 6,000 RPM using an overhead stirrer fitted with a 2-inch (5.1-cm) diameter stirring paddle. Sufficient isocyanate was then added to achieve the desired Isocyanate Index, and the formulation was mixed well for about 6 seconds (s) at about 6,000 RPM using the same stirrer. The 32-oz cup was dropped through a hole in the bottom of a 128-oz (3804 ml) paper cup on a stand. The hole was sized appropriately to catch the lip of the 32-oz cup. The total volume of the foam container was about 160 oz (4755 ml). Foams approximated this volume at the end of the foam forming reaction. Foam height over time was recorded. String gel time and tack free time were measured manually with a wooden stick and chronometer. Start time and rise time were determined with automated rate of rise equipment.

In the following examples, various types and quantities of catalysts were used to produce PIR/PUR foams of the present invention. Although the amounts of each catalyst are not the same in these examples, the respective catalyst quantities were chosen to provide similar string gel times. PIR/PUR foam properties are typically compared at equivalent string gel times. In these examples, unless otherwise specified, the pphp values listed for the carboxylate salt catalysts exclude the additional weight of the diluent. Table I lists the components of the foam formulation and their respective pphp that are used in the examples.

TABLE I Formulations of Foams in Examples 1-5 (catalyst varied) COMPONENT PARTS Polyester Polyol 100 TCPP 4.7 Surfactant 1.7 Polycat ® 5 catalyst 0.15 n-Pentane 17 Trimer Catalyst Varied Isocyanate Index Index 270 or 500

Comparative Example 1

Comparison of a Carboxylate Salt Catalyst with Standard Catalysts

Carboxylate salt catalyst 1 (an alkali metal carboxylate salt) was prepared by dissolving about 60 grams of KOH in about 150 grams of ethylene glycol. The solution was then neutralized by the addition of about 109.2 grams of pivalic acid. The water from neutralization was then removed at about 80° C. under vacuum (about 8 mmHg). The resulting approximate 50% solution of potassium pivalate (about 2 pphp or 2 grams excluding diluent; about 14.3 mmol) in ethylene glycol constituted catalyst 1. Foams were made using the standard formulation in Table I at an Isocyanate Index of about 500.

Catalyst 1 was compared with two commercial standards, the DABCO® K15 catalyst (70% potassium octoate solution) and the DABCO TMR® catalyst (75% 2-hydroxypropyltrimethylammonium octoate solution). Approximately 4.6 pphp of the DABCO® K15 catalyst were used; excluding diluent, this converts to about 3.2 pphp or 3.2 grams (about 17.7 mmol) of potassium octoate. Approximately 4.8 pphp of the DABCO TMR® catalyst were used; excluding diluent, this converts to about 3.6 pphp or 3.6 grams (about 13.8 mmol) of 2-hydroxypropyltrimethylammonium octoate. At a fairly equivalent string gel time, Table II shows foam parameters such as start time, string gel time, height of string gel time (HSG), rise time and tack free time, for catalyst 1 and the standard catalysts. The tack free time for catalyst 1 is the slightly higher when compared with the DABCO TMR® catalyst or the DABCO® K15 catalyst suggesting slightly slower surface curing time.

FIG. 1 compares the foam height versus time for catalyst 1, the DABCO® K15 catalyst, and the DABCO TMR® catalyst. The DABCO® K15 catalyst and catalyst 1 are both alkali metal carboxylate salt catalysts. Catalyst 1 has a slightly more uniform slope and less pronounced plateau as compared to the DABCO® K15 catalyst. However, it does not have the smooth profile of foam height versus time that is characteristic of the DABCO TMR® catalyst (2-hydroxylpropyltrimethylammonium octoate).

FIG. 2 depicts graphically that catalyst 1 has a smaller trimerization “step” as compared to that of potassium octoate (DABCO® K15 catalyst). The DABCO® K15 catalyst has a long valley in between the two peaks, indicating the different foam rise speeds associated with foam production using this catalyst. Neither the DABCO® K15 catalyst nor catalyst 1 has a short valley between the peaks like the DABCO TMR® catalyst; this short valley is indicative of a less significant trimerization step and a more consistent foam rise speed throughout foam production.

Comparative Example 2

Comparison of an α,β-Unsaturated Carboxylate Salt Catalyst with Standard Catalysts

α,β-unsaturated carboxylate salt catalyst 2 was prepared by dissolving about 57.5 grams of KOH in about 200 grams of ethylene glycol. The solution was then neutralized by the addition of about 64.8 grams of acrylic acid. The water from neutralization was then removed at about 80° C. under vacuum (about 8 mmHg). The resulting approximate 33% solution of potassium acrylate (about 3.3 pphp or 3.3 grams excluding diluent; about 30 mmol) in ethylene glycol constituted catalyst 2. Foams were made using the standard formulation in Table I at an Isocyanate Index of about 500.

Catalyst 2 was compared with two commercial standard catalyst solutions, the DABCO® K15 catalyst and the DABCO TMR® catalyst. Approximately 4.6 pphp of the DABCO® K15 catalyst were used; excluding diluent, this converts to about 3.2 pphp or 3.2 grams (about 17.7 mmol) of potassium octoate. Approximately 4.8 pphp of the DABCO TMR® catalyst were used; excluding diluent, this converts to about 3.6 pphp or 3.6 grams (about 13.8 mmol) of 2-hydroxypropyltrimethylammonium octoate. As shown in Table II, it was not possible to match the string gel time of catalyst 2 with either of the two standards, even when comparative catalyst 2 was introduced at levels as high as about 3.3 pphp. The poor surface cure of catalyst 2 is evidenced by the long tack free time of about 130 seconds in Table II.

FIG. 3 compares the foam height versus time for catalyst 2, the DABCO® K15 catalyst, and the DABCO TMR® catalyst. The foam height versus time curve emphasizes the very low catalytic activity of catalyst 2 relative to both the DABCO® K15 catalyst and the DABCO TMR® catalyst at an Isocyanate Index of about 500. Foam produced using catalyst 2 also showed very strong disturbances on the surface.

Inventive Example 3

Comparison of an Inventive Catalyst Comprising an α,β-Unsaturated Carboxylate Salt and a Second Carboxylate Salt with Standard Catalysts

Inventive catalyst 3 was prepared by mixing catalyst 1 (a second carboxylate salt; in this case, an alkali metal carboxylate salt) and catalyst 2 (an α,β-unsaturated carboxylate salt) in an approximate 9 to 1 weight ratio including the diluent. Excluding the diluent, the weight ratio of the catalyst components was about 14 to 1. Inventive catalyst 3 consisted of about 2 pphp or 2 grams (about 14.3 mmol) of potassium pivalate and about 0.145 pphp or 0.145 grams (about 1.3 mmol) of potassium acrylate in ethylene glycol. The approximate 14:1 weight ratio blend of the catalyst components converts to an approximate 11:1 molar ratio of the second carboxylate salt to the α,β-unsaturated carboxylate salt.

Inventive catalyst 3 was compared with two commercial standards, the DABCO® K15 catalyst and the DABCO TMR® catalyst, at an Isocyanate Index of about 500. As shown in Table II, at a similar string gel time, inventive catalyst 3 had a shorter tack free time than either the DABCO® K15 catalyst or the DABCO TMR® catalyst. Since tack free time is a measure of surface cure, catalyst 3 has a faster surface cure, which would correlate with improved surface adhesion in foam laminations. The fast surface cure of inventive catalyst 3 as measured by the tack free time is also unexpected given the tack free time of the individual components that make up inventive catalyst 3. Catalyst 1 had a tack free time of about 69 seconds and catalyst 2 showed a tack free time of about 130 seconds—and had very low catalytic activity. Inventive catalyst 3 showed a tack free time of about 54 seconds, much less than either catalyst 1 or catalyst 2 independently.

Inventive catalyst 3 also provides faster surface cure when compared to the commercially available catalyst systems, either the DABCO® K15 catalyst and or the DABCO TMR® catalyst, such that the foam products made with the catalyst 3 would have enhanced surface adherence during the manufacture of finished products such as laminated foam panels.

FIG. 4 compares the foam height versus time for inventive catalyst 3, the DABCO® K15 catalyst, and the DABCO TMR® catalyst. Inventive catalyst 3 has a uniform slope and minimal plateau that is normally associated with that of the DABCO TMR® catalyst. This consistent increase in foam height versus time is highly desired for continuous foam production operations.

The shapes of the curves of inventive catalyst 3 and the DABCO TMR® catalyst are very similar in FIG. 5, further illustrating that inventive catalyst 3 would have foam processing performance similar to that of the DABCO TMR® catalyst. These foam rise speed profiles indicate a more consistent foam rise over time and improved foam production performance in continuous operations. Further, inventive catalyst 3 has thermal stability to over 150° C. and can produce a PIR/PUR foam which is substantially free of volatile amines and/or amine odors.

TABLE II Comparison of catalysts 1-3 to standard catalysts Tack String Gel Rise Free Start Time Time HSG Time Time Catalyst [s] [s] [%] [s] [s] ^(a)4.6 pphp DABCO ® K15 13 44 90 61 61 ^(b)4.8 pphp DABCO TMR ® 20 44 83 50 60 ^(c)2 pphp Catalyst 1 22 52 83 70 69 ^(c)3.3 pphp Catalyst 2 40 108 88 140 130 ^(c)2.1 pphp Catalyst 3 19 46 88 58 54 Notes: ^(a)4.6 pphp DABCO ® K15 catalyst including diluent converts to about 3.2 pphp of potassium octoate salt catalyst excluding diluent. ^(b)4.8 pphp DABCO TMR ® catalyst including diluent converts to about 3.6 pphp of 2-hydroxypropyltrimethylammonium octoate catalyst excluding diluent. ^(c)Catalyst 1-3 pphp values exclude the diluent.

Inventive Example 4

Comparison of an Inventive Catalyst Comprising an α,β-Unsaturated Carboxylate Salt and a Second Carboxylate Salt (Potassium Octoate) with the Standard DABCO® K15 Potassium Octoate Catalyst

Inventive catalysts were prepared by mixing a potassium acrylate solution (an α,β-unsaturated carboxylate salt; catalyst 2) with a second carboxylate salt solution in varying weight ratios. The second carboxylate salt was potassium octoate, an alkali metal carboxylate salt commercially available in solution as the DABCO® K15 catalyst. Foams were made using the standard formulation in Table I at an Isocyanate Index of about 270.

As shown at a similar string gel time in Table III, the tack free time decreases as the amount of catalyst 2 (potassium acrylate) increases relative to the amount of the DABCO® K15 catalyst (potassium octoate). The weight ratios are shown both including and excluding the contribution of the diluent. In this example, higher relative amounts of the α,β-unsaturated carboxylate salt, potassium acrylate, translate to a faster surface cure and consequently, better foam adhesion in lamination.

TABLE III Foam parameters at different weight ratios of K15/catalyst 2 Mixture Excluding Diluent K15 19:1 6:1 2:1 1:1.4 1:4 Cat. 2 PPHP 1.47 1.46 1.52 1.55 1.52 1.54 1.45 Mixture Including Diluent K15 9:1 3:1 1:1 1:3 1:9 Cat. 2 PPHP 2.1 2.2 2.5 3.0 3.6 4.2 4.4 Start Time (s) 15 15 16 14 18 22 26 String Gel 55 53 51 51 51 55 58 Time (s) Rise Time (s) 75 71 68 70 70 84 97 Tack Free 112  102  90 82 70 72 69 Time (s)

FIG. 6 compares the foam height versus time for several weight ratios, excluding diluent, of the DABCO® K15 catalyst to catalyst 2, and that of the DABCO TMR® catalyst. The DABCO TMR® catalyst was used at about 2.9 pphp (about 2.2 pphp excluding the diluent). As the amount of catalyst 2 (potassium acrylate) increased relative to the amount of the DABCO® K15 catalyst (potassium octoate), a smoother profile of foam height versus time resulted. The K15/catalyst 2 ratios of about 1:1.4 and about 1:4 had uniform slopes and less pronounced plateaus, similar to the DABCO TMR® catalyst. This is indicative of a more consistent foam rise over time, desirable for continuous foam operations.

The 1:1.4 weight ratio blend of K15/catalyst 2 (diluent excluded) converts to an approximate 1:2.3 molar ratio of the second carboxylate salt to the α,β-unsaturated carboxylate salt. Similarly, the 1:4 weight ratio blend of K15/catalyst 2 (diluent excluded) converts to an approximate 1:7 molar ratio of the second carboxylate salt to the α,β-unsaturated carboxylate salt.

Inventive Example 5

Comparison of an Inventive Catalyst Comprising an α,β-unsaturated Carboxylate Salt and a Second Carboxylate Salt (Potassium Acetate) with the Standard DABCO® K2097 Potassium Acetate Catalyst

Inventive catalysts were prepared by mixing a potassium acrylate solution (an α,β-unsaturated carboxylate salt; catalyst 2) with a second carboxylate salt solution in varying weight ratios. The second carboxylate salt was potassium acetate, an alkali metal carboxylate salt commercially available in solution as the DABCO® K2097 catalyst. Foams were made using the standard formulation in Table I at an Isocyanate Index of about 270.

As shown in Table IV, a tack free time of about 58 seconds was obtained at a K2097/catalyst 2 weight ratio—excluding diluent—of about 2.7:1. This catalyst combination of a second carboxylate salt (in this case, an alkali metal carboxylate salt) and an α,β-unsaturated carboxylate salt gave the shortest tack free time, indicating faster surface cure and consequently, better adhesion performance in laminated foam structure. The 2.7:1 weight ratio blend of K2097/catalyst 2 (diluent excluded) converts to an approximate 3:1 molar ratio of the second carboxylate salt to the α,β-unsaturated carboxylate salt.

TABLE IV Foam parameters at different weight ratios of K2097/catalyst 2 Mixture Excluding Diluent K2097 8:1 2.7:1 1:1 1:3.3 1:10 Cat. 2 PPHP 0.9 0.97 1.05 1.13 1.35 1.47 1.45 Mixture Including Diluent K2097 9:1 3:1 1:1 1:3 1:9 Cat. 2 PPHP 3.0 3.2 3.4 3.6 4.2 4.5 4.4 Start Time (s) 17 18 16 19 19 22 26 String Gel 47 47 45 49 50 57 58 Time (s) Rise Time (s) 60 60 58 65 68 77 97 Tack Free 68 62 58 61 63 71 69 Time (s) 

The invention claimed is:
 1. A catalyst composition comprising the contact product of a) at least one α,β-unsaturated carboxylate salt having a formula:

wherein X, Y, and Z are selected independently from a C₁-C₃₆ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; —CO₂H; —CO₂M¹; or a hydrogen atom; and wherein M¹ in each occurrence is a tetraalkylammonium ion selected from the group consisting of tetramethylammonium, tetraethylammonium, tetrapropylammonium, tetrabutylammonium and combinations thereof; and b) at least one second carboxylate salt; wherein the catalyst composition is thermally stable at a temperature up to about 150° C.
 2. The catalyst composition of claim 1, wherein X, Y, and Z are selected independently from a hydrogen atom, methyl, ethyl, propyl, butyl, pentyl, hexyl, phenyl, tolyl, benzyl, —CO₂H, or —CO₂M¹.
 3. The catalyst composition of claim 1, wherein the at least one α,β-unsaturated carboxylate salt is a salt of acrylic acid, methacrylic acid, fumaric acid, maleic acid, or any combination thereof.
 4. The catalyst composition of claim 1, wherein the at least one α,β-unsaturated carboxylate salt is tetramethylammonium acrylate, tetraethylammonium acrylate, tetrapropylammonium acrylate, tetrabutylammonium acrylate, tetramethylammonium methacrylate, tetraethylammonium methacrylate, tetrapropylammonium methacrylate, tetrabutylammonium methacrylate, mono-tetramethylammonium fumarate, bis-tetramethylammonium fumarate, mono-tetraethylammonium fumarate, bis-tetraethylammonium fumarate, mono-tetrapropylammonium fumarate, bis-tetrapropylammonium fumarate, mono-tetrabutylammonium fumarate, bistetrabutylammonium fumarate, mono-tetramethylammonium maleate, bis-tetramethylammonium maleate, mono-tetraethylammonium maleate, bis-tetraethylammonium maleate, mono-tetrapropylammonium maleate, bistetrapropylammonium maleate, monotetrabutylammonium maleate, bis-tetrabutylammonium maleate, or any combination thereof.
 5. The catalyst composition of claim 1, wherein the catalyst composition, when in the presence of an isocyanate, trimerizes the isocyanate to produce an isocyanurate.
 6. The catalyst composition of claim 1, further comprising at least one urethane catalyst.
 7. The catalyst composition of claim 1, wherein the weight ratio of the at least one α,β-unsaturated carboxylate salt to the at least one second carboxylate salt is from about 0.02:1 to about 50:1.
 8. The catalyst composition of claim 7, wherein the weight ratio of the at least one α,β-unsaturated carboxylate salt to the at least one second carboxylate salt is from about 0.05:1 to about 20:1.
 9. The catalyst composition of claim 8, wherein the weight ratio of the at least one α,β-unsaturated carboxylate salt to the at least one second carboxylate salt is from about 0.1:1 to about 10:1.
 10. The catalyst composition of claim 1, wherein the at least one second carboxylate salt is: (a) an alkali metal carboxylate salt; (b) an alkaline earth metal carboxylate salt; (c) a quaternary ammonium carboxylate salt, or any combination thereof.
 11. The catalyst composition of claim 1 wherein the at least one second carboxylate salt is a salt of formic acid, acetic acid, propionic acid, butanoic acid, butyric acid, isobutyric acid, pivalic acid, pentanoic acid, hexanoic acid, neohexanoic acid, heptanoic acid, neoheptanoic acid, octanoic acid, neooctanoic acid, 2-ethyl-hexanoic acid, nonanoic acid, neononanoic acid, decanoic acid, neodecanoic acid, undecanoic acid, neoundecanoic acid, dodecanoic acid, neododecanoic acid, myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid, linolenic acid, ricinoleic acid, or any combination thereof.
 12. The catalyst composition of claim 10, wherein the at least one second carboxylate salt is potassium pivalate, potassium formate, potassium acetate, potassium propionate, potassium butanoate, potassium pentanoate, potassium hexanoate, potassium neohexanoate, potassium heptanoate, potassium octoate, potassium neooctoate, potassium decanoate, potassium butyrate, potassium isobutyrate, potassium nonante, potassium stearate, potassium neodecanoate, potassium neoheptanoate, sodium octoate, lithium stearate, sodium caprioate, lithium octoate, or any combination thereof.
 13. The catalyst composition of claim 12, wherein the at least one second carboxylate salt is potassium pivalate, potassium acetate, potassium octoate, or any combination thereof.
 14. The catalyst composition of claim 1, wherein the at least one second carboxylate salt has a formula: A-CO₂M² wherein A is a hydrogen atom, or a C₁-C₁₇ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; and wherein M² is: (i) an alkali metal ion, (ii) an alkaline earth metal ion, or (iii) a quaternary ammonium ion.
 15. The catalyst composition of claim 14, wherein A is a hydrogen atom, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, or octyl.
 16. The catalyst composition of claim 14, wherein M² is an ion of lithium, potassium, sodium, rubidium, magnesium, or calcium, or a quaternary ammonium ion.
 17. The catalyst composition of claim 16, wherein M² is a potassium ion.
 18. The catalyst composition of claim 16, wherein the quaternary ammonium ion is tetramethylammonium, tetraethylammonium, tetrapropylammonium, or tetrabutylammonium.
 19. The catalyst composition of claim 1 wherein the contact product comprises tetramethylammonium acrylate and at least one second carboxylate salt having a formula: A-CO₂M², wherein: A is a hydrogen atom, or a C₁-C₁₇ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; and M² is: (i) an alkali metal ion, or, (ii) a quaternary ammonium ion.
 20. The catalyst composition of claim 1 wherein the contact product comprises tetramethylammonium acrylate; and at least one member selected from the group consisting of potassium pivalate, potassium acetate, and potassium octoate.
 21. The catalyst composition of claim 1 wherein the contact product comprises at least one α,β-unsaturated carboxylate salt having the formula

wherein: X, Y, and Z are selected independently from a C₁-C₃₆ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; —CO₂H; —CO₂M¹; or a hydrogen atom; and M¹ in each occurrence is tetraalkylammonium ion selected from the group consisting of tetramethylammonium, tetraethylammonium, tetrapropylammonium, tetrabutylammonium and combinations thereof, and wherein the at least one α,β-unsaturated carboxylate salt comprises a salt of at least one of acrylic acid and methacrylic acid; and at least one second carboxylate salt having a formula A-CO₂M² wherein: A is a hydrogen atom, or a C₁-C₁₇ alkyl, alkenyl, aryl, or aralkyl, any of which are substituted or unsubstituted; and M² is potassium or a quaternary ammonium ion, and the second carboxylate salt comprises a salt of at least one acid selected from the group consisting of formic, acetic, propionic, butanoic, butyric, isobutyric, pivalic, pentanoic, hexanoic, neohexanoic, heptanoic, neoheptanoic, octanoic, neooctanoic, 2-ethyl-hexanoic, nonanoic, neononanoic, decanoic, neodecanoic, undecanoic, neoundecanoic, dodecanoic, neododecanoic, myristic, palmitic, stearic, oleic, linoleic, linolenic, and ricinoleic.
 22. The catalyst composition of claim 1 further comprising at least one blowing agent.
 23. The catalyst composition of claim 1 further comprising at least one diluent.
 24. The catalyst composition of claim 10 wherein the at least one second carboxylate salt comprises a potassium carboxylate salt.
 25. The catalyst composition of claim 24 wherein X, Y, and Z are selected independently from —CO₂H; —CO₂M¹ or a hydrogen atom. 